Using high-k dielectrics in isolation structures method, pixel and imager device

ABSTRACT

An imager device that has an isolation structure such that pinned photodiode characteristics are maintained without increasing doping levels. The invention provides an isolation structure to maintain pinned photodiode characteristics without increasing doping levels around the photodiode. By creating a substrate region surrounding the charge-collection region of the photodiode, the photodiode may be electrically isolated from the bulk substrate. This region fixes the depletion region so that it does not migrate toward the surface of the substrate or the STI region. By doing so, the region prevents charge from being depleted from the substrate and the accumulation region, reducing dark current.

FIELD OF THE INVENTION

The invention relates to the field of semiconductor devices and, in particular, to a pixel cell using a high-k dielectric film to create a strong accumulation region for providing isolation and optimizing characteristics of the cell.

BACKGROUND OF THE INVENTION

A CMOS imager circuit includes a focal plane array of pixel cells, each cell includes a photosensor, for example, a photogate, photoconductor or a photodiode overlying a substrate for producing a photo-generated charge in a doped region of the substrate. A readout circuit is provided for each pixel cell and includes at least a source follower transistor and a row select transistor for coupling the source follower transistor to a column output line. The pixel cell also typically has a floating diffusion node, connected to the gate of the source follower transistor. Charge generated by the photosensor is sent to the floating diffusion region. The imager may also include a transistor for transferring charge from the photosensor to the floating diffusion node and another transistor for resetting the floating diffusion region node to a predetermined charge level prior to charge transference. Each pixel cell is isolated from other pixel cells in the array by a field oxide region (STI), which surrounds it and separates the doped regions of the substrate within that pixel cell from the doped regions of the substrate within neighboring pixel cells.

In a CMOS imager, the active elements of a pixel cell, for example a four transistor pixel, perform the necessary functions of (1) photon to charge conversion; (2) transfer of charge to the floating diffusion node; (3) resetting the floating diffusion node to a known state before the transfer of charge to it; (4) selection of a pixel cell for readout; and (5) output and amplification of a signal representing a reset voltage and a pixel signal voltage based on the photo converted charges. The charge at the floating diffusion node is converted to a pixel output voltage by a source follower output transistor.

FIG. 1 illustrates a block diagram of a CMOS imager device 100 having a pixel array 110 with each pixel cell being constructed as described above. Pixel array 110 comprises a plurality of pixels arranged in a predetermined number of columns and rows (not shown). The pixels of each row in array 110 are all turned on at the same time by a row select line, and the pixels of each column are selectively output by respective column select lines. A plurality of row and column lines are provided for the entire array 110. The row lines are selectively activated by the row driver 145 in response to row address decoder 155 and the column select lines are selectively activated by the column driver 160 in response to column address decoder 170. Thus, a row and column address is provided for each pixel.

The CMOS imager is operated by a control circuit 150, which controls decoders 155, 170 for selecting the appropriate row and column lines for pixel readout, and row and column driver circuitry 145, 160, which apply driving voltage to the drive transistors of the selected row and column lines. The pixel column signals, which typically include a pixel reset signal Vrst and a pixel image signal Vsig for each pixel are read by sample and hold circuitry 161, 162 associated with the column device 160. A differential signal Vrst-Vsig is produced for each pixel, which is amplified and digitized by analog-to-digital converter 175. The analog to digital converter 175 converts the analog pixel signals to digital signals which, are fed to an image processor 180 to form a digital image.

Exemplary CMOS imaging circuits, processing steps thereof, and detailed descriptions of the functions of various CMOS elements of an imaging circuit are described, for example, in U.S. Pat. No. 6,140,630, U.S. Pat. No. 6,376,868, U.S. Pat. No. 6,310,366, U.S. Pat. No. 6,326,652, U.S. Pat. No. 6,204,524, and U.S. Pat. No. 6,333,205, assigned to Micron Technology, Inc. The disclosures of each of the forgoing are hereby incorporated by reference herein in their entirety.

A schematic diagram of an exemplary CMOS four-transistor (4T) pixel cell 10 is illustrated in FIG. 2. The four transistors include a reset transistor 34, source follower transistor 36, row select transistor 38 and a transfer gate 32. A photosensor 40 converts incident light into an electrical charge. A floating diffusion region 50 receives the charge from the photosensor 40 through the transfer gate 32 (when activated by a transfer gate control signal TG) and is connected to the reset transistor 34 and the gate of the source follower transistor 36. The source follower transistor 36 outputs a signal proportional to the charge accumulated in the floating diffusion region 50 when the row select transistor 38 is turned on. The reset transistor 34 resets the floating diffusion region 50 (when activated by a reset control signal RST) to a known potential prior to transfer of charge from the photosensor 40. The photosensor 40 may be a photodiode, photogate, or photoconductor. If a photodiode is employed, the photodiode may be formed below a surface of the substrate and may be a buried PNP photodiode, buried NPN photodiode, a buried PN photodiode, or a buried NP photodiode, among others.

In a conventional CMOS imager pixel with a buried photodiode, the photodiode converts incident light to an electrical charge. The photodiode accumulates this charge throughout the sampling period. At the end of the sampling period, the transfer gate closes (i.e., is activated) and the charge is drained from the photodiode through the transfer gate.

A buried photodiode has a shallow implant of a first conductivity (referred to herein as an accumulation region) above a deeper implant of another conductivity (referred to herein as a charge-collection region) in a substrate lightly doped with the first conductivity type. A depletion region exists at the interface between the accumulation region and the charge collection region. For example, in a p-type substrate, a shallow low-dose p-type implant is applied over an n-type photosensitive region. This also produces a dual-junction sandwich that alters the visible light spectral response (the sensitivity to optical radiation of different wavelengths) of the pixel. The upper junction is optimized for responding to lower wavelengths while the lower junction is more sensitive to the longer wavelengths.

However, the top surface of the photodiode is electrically connected to the bulk substrate via a portion of the accumulation region above the charge-collection region and a portion of the accumulation region between the field oxide region (referred to hereinafter as a STI region) and the charge-collection region. The depletion of charge from the substrate and accumulation region causes excessive leakage and creates a false signal, commonly known as “dark current.” Dark current is a current that is created without photoconversion of light. Dark current may be reduced by preventing depletion of the accumulation region.

Attempts to overcome a depletion of the accumulation region have involved increasing the doping level near the STI sidewall. However, increasing the doping level near the STI sidewall creates excess leakage, which is quite significant in the overall dark current leakage level in a pinned photodiode.

Therefore, it is desirable to create an isolation structure where pinned photodiode characteristics are maintained without increased doping levels.

BRIEF SUMMARY OF THE INVENTION

The invention provides an isolation structure to maintain pinned photodiode characteristics without increasing doping levels around the photodiode. By creating a substrate region surrounding the charge-collection region of the photodiode, the photodiode may be electrically isolated from the bulk substrate. This region fixes the depletion region so that it does not migrate toward the surface of the substrate or the STI region. By doing so, the region prevents charge from being depleted from the substrate and the accumulation region, reducing dark current.

The region is achieved by depositing a high-k dielectric material on the surface of the substrate above the photodiode and on the sidewalls of the STI trench. The high-k dielectric material induces excess charge on the surface of the substrate above the photodiode and in the sidewalls of the STI region adjacent to the photodiode.

Aluminum oxide is one high-k dielectric material (a material with a dielectric constant greater than that of silicon dioxide) that induces an excess negative charge, as noted in Manchanda et al., “Si-Doped Aluminates for High Temperature Metal-Gate CMOS: Zr—Al—Si—O, A Novel Gate Dielectric for Low Power Applications,” IEEE IEDM Technical Digest (2000) pp.23-26; Lee et al., “Effect of Polysilicon Gate on the Flatband Voltage Shift and Mobility Degradation for ALD-Al₂O₃ Gate Dielectric,” IEEE IEDM Technical Digest (2000) pp. 645-648; and Buchanan et al., “80 nm poly-silicon gated n-FETs with ultra-thin Al₂O₃ gate dielectric for ULSI applications,” IEEE IEDM Technical Digest (2000) pp. 223-226.

Because of these properties, when using, for example, aluminum oxide (or other high-k dielectric material) to line or fill the STI regions and cover the surface of the substrate overlying a PNP photodiode, there will be an excess negative charge in the aluminum oxide layers that induces and maintains a hole-accumulation region between the aluminum oxide layer and the charge-collection region of the photodiode. Similarly, when using a high-k dielectric material in the STI trenches and on the surface of the substrate overlying an NPN photodiode, there will be an excess positive charge in the high-k dielectric material that induces and maintains an electron-rich accumulation region. By maintaining the accumulation region, the depletion region between the accumulation region and the charge-collection region is prevented from migrating toward the STI regions and the substrate surface, thereby electrically isolating the photodiode and decreasing charge leakage from the bulk substrate into the photodiode.

BRIEF DESCRIPTION OF THE DRAWINGS

Additional advantages and features of the present invention will be apparent from the following detailed description and drawings which include various embodiments of the invention, in which:

FIG. 1 is a block diagram of an imaging device;

FIG. 2 is a schematic diagram of a four-transistor (4T) pixel;

FIG. 3 a cross-section of an exemplary pixel cell of the present invention at an initial stage of fabrication;

FIG. 4 is an illustration of the pixel cell of FIG. 3 at a subsequent stage of fabrication;

FIG. 5 is an illustration of the pixel cell of FIG. 4 at a subsequent stage of fabrication;

FIG. 6 is an illustration of the pixel cell of FIG. 5 at a subsequent stage of fabrication;

FIG. 7 is an illustration of the pixel cell of FIG. 6 at a subsequent stage of fabrication;

FIG. 8 is an illustration of the pixel cell of FIG. 7 at a subsequent stage of fabrication;

FIG. 9 is an illustration of the pixel cell of FIG. 8 at a subsequent stage of fabrication;

FIG. 10 a is an illustration of the pixel cell of FIG. 9 at a subsequent stage of fabrication;

FIG. 10 b is an illustration of the pixel cell of FIG. 7 at an alternative subsequent stage of fabrication;

FIG. 10 c is an illustration of the pixel cell of FIG. 7 at an alternative subsequent stage of fabrication;

FIG. 11 a is an illustration of the pixel cell of FIG. 10 a at a subsequent stage of fabrication;

FIG. 11 b is an illustration of the pixel cell of FIG. 10 a at an alternative subsequent stage of fabrication;

FIG. 12 is an illustration of the pixel cell of FIG. 11 a at a subsequent stage of fabrication;

FIG. 13 is an illustration of the pixel cell of FIG. 12 at a subsequent stage of fabrication;

FIG. 14 is an illustration of the pixel cell of FIG. 13 at a subsequent stage of fabrication;

FIG. 15 is an illustration of the pixel cell of FIG. 14 at a subsequent stage of fabrication;

FIG. 16 is an illustration of the pixel cell of FIG. 15 at a subsequent stage of fabrication;

FIG. 17 is an illustration of the pixel cell of FIG. 16 at a final stage of fabrication; and

FIG. 18 shows a processor system incorporating at least one imager device constructed in accordance with an embodiment of the invention.

DETAILED DESCRIPTION OF THE INVENTION

In the following detailed description, reference is made to the accompanying drawings which form a part hereof, and in which is shown by way of illustration specific embodiments in which the invention may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the invention, and it is to be understood that other embodiments may be utilized, and that structural, logical and electrical changes may be made without departing from the spirit and scope of the present invention. Additionally, processing steps described and their progression are exemplary of preferred embodiments of the invention. However, the sequence of steps is not limited to that set forth herein and may be changed as is known in the art, with the exception of steps necessarily occurring in a certain order.

The term “substrate” is to be understood as a semiconductor-based material including silicon, silicon-on-insulator (SOI) or silicon-on-sapphire (SOS) technology, doped and undoped semiconductors, epitaxial layers of silicon supported by a base semiconductor foundation, and other semiconductor structures. Furthermore, when reference is made to a “substrate” in the following description, previous process steps may have been utilized to form regions or junctions in the base semiconductor structure or foundation. In addition, the semiconductor need not be silicon-based, but could be based on silicon-germanium, germanium, or gallium arsenide.

The term “pixel” refers to a photo-element unit cell containing a photosensor and transistors for converting light radiation to an electrical signal. For purposes of illustration, a representative pixel is illustrated in the figures and description herein and, typically, fabrication of all pixels in an imager will proceed simultaneously in a similar fashion. The following detailed description is not to be taken in a limiting sense, and the scope of the present invention is defined by the appended claims.

Referring now to the drawings, where like elements are designated by like reference numerals, FIG. 3 shows a pixel cell 10 an initial stage of processing in accordance with the invention. A substrate 15 with a first conductivity is provided. For the purposes of illustration, the first conductivity type is p-type. A silicon dioxide layer 22 is grown over the surface of the substrate 15.

Referring to FIG. 4, a nitride hard mask layer 23 is deposited over the silicon dioxide layer 22. The nitride hard mask layer 23 protects the active area underneath during subsequent processing steps. The nitride hard mask layer 23 is approximately 200 Å to 1000 Å in thickness.

Referring to FIG. 5, a photoresist mask 20 is formed and patterned with an opening 21. The nitride hard mask layer and the substrate then undergo an etching process to create a trench 24, as shown in FIG. 6. In this illustration, only one trench 24 is shown. However, it should be appreciated that more than one opening and trench would be formed in a pixel cell array. Trenches of about 1,000 Å to about 4,000 Å in depth, preferably about 1,500 Å to about 3,000 Å, with a width of about 500 Å to about 10,000 Å, preferably about 1,000 Å to about 3,000 Å, are typically desired. The trench 24 is formed in the substrate 15 by anisotropic etching. The photoresist mask 20 is subsequently removed, as shown in FIG. 6.

Referring to FIG. 7, a layer of silicon dioxide 22 is grown on the sidewalls of the trench 24 over the surface of the substrate 15. The silicon dioxide layer 22 in the trench 24 is optional and acts as a dielectric in the final structure. When the silicon dioxide layer 22 is grown as part of the final pixel cell 10, the layer 22 enhances the dielectric effects of the final structure. However, layer 22 may be removed before the next stage of fabrication. Growing a layer of silicon dioxide over a silicon substrate heals the defects in the surface of the silicon substrate, even if the silicon dioxide is subsequently removed. For the purposes of illustration, the embodiment without removing the silicon dioxide layer 22 shall be discussed herein.

Referring to FIG. 8, the substrate 15 is subjected to a conformal deposition process to deposit a high-k dielectric material such as, e.g., a thin aluminum oxide liner layer 26 over the silicon dioxide layer 22 on the surface of the substrate 15 and over the walls of the trench 24. Although aluminum oxide is the material used in the present embodiment, any material with a high-k dielectric constant that induces excess negative charge is suitable for this embodiment. Materials such as aluminum nitride, silicon-rich aluminum oxides, and others are also suitable. Methods such as chemical vapor deposition, atomic layer deposition, plasma vapor deposition, or other suitable techniques may be employed in forming the aluminum oxide layer 26. The aluminum oxide layer 26 is deposited to a thickness within the range of 30 Å and 500 Å, and preferably about 50 Å.

Referring to FIG. 9, an insulating layer 28 of dielectric material is deposited over the aluminum oxide layer 26, filling the trench 24. The insulating layer 28 may consist of an insulating material such as silicon dioxide, silicon nitride, oxide-nitride, nitride-oxide, oxide-nitride-oxide, or other suitable insulating material. This material is deposited within the trench 24 by chemical vapor deposition, low pressure chemical vapor deposition, or other suitable techniques. As shown in FIG. 10 a, the substrate 15 is then planarized, removing excess insulating layer 28, aluminum oxide layer 26, and silicon dioxide layer 22 above the surface of the substrate 15. Chemical mechanical polishing or RIE dry etching processes may be employed to achieve the resulting lined STI region 30.

Alternatively, FIG. 10 b illustrates an embodiment where the aluminum oxide layer 26 entirely fills the trench 24 instead of using an insulating layer 28, such that the resulting STI region 30, uses aluminum oxide as the insulating material. By eliminating the step of depositing a separate dielectric layer 28, this alternative offers additional processing simplicity. A further alternative, where the silicon dioxide layer 22 is removed prior to deposition of aluminum oxide layer 26, is shown in FIG. 10 c. For the purposes of illustration, the embodiment having an STI region 30 with a silicon dioxide layer 22, an aluminum oxide layer 26, and insulating layer 28 (FIG. 10 a) shall be discussed herein. However, the following steps may also be performed on the FIG. 10 b and 10 c embodiments.

Referring to FIGS. 11 a and 11 b, the desired gate stacks, such as the stacks for transfer gate 32, are layered, masked, and etched over the surface of the substrate 15. A photoresist 31 is formed over the substrate 15 and patterned to partially overlap the gate stack of the transfer gate 32, as shown in FIG. 11 a. A dopant implant 201 of a first conductivity type (i.e., p-type) is performed on the substrate 15, forming a p-type well 25 region having p-type ions (e.g., boron) beneath the active area of the pixel 10. Alternatively, as shown in FIG. 11 b, the dopant implant 201 may be performed without photoresist 31 and can form a blanket p-well 25 in the substrate 15. For discussion purposes only, the FIG. 11 a embodiment having a p-well region is used to describe the following stages.

Next, as shown in FIG. 12, the substrate 15 is masked with photoresist 41, leaving the portion of the substrate 15 where the photodiode is to be located exposed, and an angled ion implant 202 of a second conductivity type (i.e., n-type) is performed. This implant 202 can be performed by implanting appropriate n-type ions (e.g., arsenic, antimony, phosphorous, etc.) at an energy of about 10 KeV to about 400 KeV at an implant dosage of about 3×10¹¹ ions/cm² to about 1×10¹⁵ ions/cm², preferably 1×10¹² ions/cm² to about 1×10¹⁴ ions/cm². This implant 202 forms an n-type region 42, which is the buried layer, or the charge-collection region, of the photodiode 40.

Referring to FIG. 13, a dopant implant 203 of a first conductivity type (i.e., p-type) is performed to form a p-type region 43 over the n-type region 42. The p-type region 43 serves as the accumulation layer of the photodiode 40, pinning the potential of the photodiode 40 to a constant value when it is fully depleted. The photoresist 41 may then be removed.

As shown in FIG. 14, other conventional steps of masking and doping are performed to obtain a floating diffusion region 50 between the transfer gate 32 and the reset transistor 34 and a source/drain region 55 adjacent to the reset transistor 34.

Referring to FIG. 15, a layer of silicon dioxide 45 is grown on the surface of the substrate 15 and etched back such that it remains only over the STI region 30 and photodiode 40. As with silicon dioxide layer 22, layer 45 may be optionally removed. By forming a silicon dioxide layer over a silicon substrate and subsequently removing it, the silicon dioxide heals defects in the surface of the substrate, providing a more uniform surface. Therefore, while the embodiment having the silicon dioxide layer 45 removed would not provide the same dielectric properties as an embodiment keeping the layer 45, it would still have the benefits of providing a substrate surface which is essentially free of defects. For the purposes of illustration, the embodiment without removing silicon dioxide layer 45 shall be discussed herein.

Referring to FIG. 16, a thin aluminum oxide film 46 is selectively deposited over silicon dioxide layer 45 on the surface of the substrate 15, over the STI region 30 and photodiode 40, by methods such as chemical vapor deposition, atomic layer deposition, plasma vapor deposition, or other suitable techniques. The aluminum oxide film 46 may be deposited to a thickness within the range of about 30 Å to about 500 Å, preferably about 50 Å. A photo step may remove any excess aluminum oxide film from surfaces other than the tops of the STI region 30 and the photodiode 40. Although the aluminum oxide film 46 is described as being deposited after the formation of the photodiode 40, it may also be deposited before or after the formation of the photodiode 40, depending on desired sequence of processing.

The high-k dielectric films (e.g., aluminum oxide, aluminum nitride, silicon-rich aluminum oxides) create a very shallow accumulation layer over the photodiode 40 and near the sidewalls of the STI region 30. Aluminum oxide induces an excess negative charge in the sidewalls of the STI region 30 and above the photodiode 40. Negative charge in these regions results in hole accumulation in the p-type regions of the substrate. This electrically disconnects the photodiode 40 from the bulk substrate 15, preventing depletion of the substrate 15 and excessive leakage.

A spacer insulating layer 33 (FIG. 17) is deposited over the pixel cell 10 and other conventional processing steps, such as conductive line formation to pixel cell 10, may follow.

Although the above embodiments have been described with reference to the formation of n-channel devices, it must be understood that the invention is not limited to this embodiment. Accordingly, the invention has equal applicability to p-channel devices formed within an n-type substrate 15. In such an embodiment the conductivity types of all structures changes accordingly. For example, in FIG. 17, aluminum oxide layers 26, 46 are replaced with layers 26, 46, having excess positive charge (e.g., silicon nitride), to induce electron-rich accumulation regions in the n-type region 43 and the n-type substrate 15 surrounding the p-type region 42 of the photodiode 40.

FIG. 18 shows a system 300, a typical processor-based system modified to include an imager device 100, as in FIG. 1, employing pixels of the present invention. Examples of processor-based systems, which may employ the imager device 100, include, without limitation, computer systems, camera systems, scanners, machine vision systems, vehicle navigation systems, video telephones, surveillance systems, auto focus systems, star tracker systems, motion detection systems, image stabilization systems, and others.

System 300 includes a central processing unit (CPU) 302 that communicates with various devices over a bus 304. Some of the devices connected to the bus 304 provide communication into and out of the system 300, illustratively including an input/output (I/O) device 306 and imager device 100. Other devices connected to the bus 304 provide memory, illustratively including a random access memory system (RAM) 310, hard drive 312, and one or more peripheral memory devices such as a floppy disk drive 314 and compact disk (CD) drive 316. The imager device 100 may be combined with a processor, such as a CPU, digital signal processor, or microprocessor, in a single integrated circuit. The imager device 100 may be a CCD imager or CMOS imager constructed in accordance with any of the illustrated embodiments.

The above description and drawings are only to be considered illustrative of exemplary embodiments which achieve the features and advantages of the invention. Modification of, and substitutions to, specific process and conditions and structures can be made without departing from the spirit and scope of the invention. Accordingly, the invention is not to be considered as being limited by the foregoing description and drawings, but is only limited by the scope of the appended claims. 

1. A pixel cell comprising: a substrate; a photosensor in said substrate, said photosensor including a first conductivity area below a surface of said substrate and a second conductivity area at least between said first conductivity area and said substrate surface; and a first layer having an excess charge sufficient to create an electric field that affects said second conductivity area.
 2. The pixel cell of claim 1, wherein said photosensor is a pinned photodiode.
 3. The pixel cell of claim 1, further comprising an isolation region spaced from said photosensor, wherein said isolation region has a bottom and sidewalls with said first layer deposited thereon.
 4. The pixel cell of claim 3, further comprising a second layer on a surface of said substrate over said isolation region and said photosensor.
 5. The pixel cell of claim 4, wherein said second layer has an excess charge sufficient to create an electric field which affects said second conductivity area.
 6. The pixel cell of claim 5, wherein said first and second layers comprise a high-k dielectric material.
 7. The pixel cell of claim 6, wherein said high-k dielectric material has an excess negative charge.
 8. The pixel cell of claim 6, wherein said high-k dielectric material is selected from the group consisting of aluminum oxide, aluminum nitride, and aluminum silicates.
 9. The pixel cell of claim 5, wherein said second conductivity area maintains holes at said substrate surface and at a surface of said isolation region sidewall.
 10. The pixel cell of claim 5, wherein said field prevents a depletion region of said photodiode from reaching at least one of said STI region and said substrate surface.
 11. The pixel cell of claim 6, wherein said high-k dielectric material has an excess positive charge.
 12. The pixel cell of claim 11, wherein said second conductivity area maintains electrons at said substrate surface and at a surface of said STI region sidewall.
 13. The pixel cell of claim 11, wherein said second conductivity area accumulates electrons.
 14. The pixel cell of claim 5, further comprising a dielectric layer between said layer of high-k dielectric material and said substrate.
 15. The pixel cell of claim 14, wherein said dielectric layer comprises silicon dioxide.
 16. A pixel cell comprising: a substrate having a first conductivity type; a pinned photodiode in said substrate and having a charge collection region of a second conductivity type and an accumulation region of said first conductivity type at least over said charge collection region; and an isolation trench adjacent to said pinned photodiode, wherein sidewalls of said isolation trench have a charge density sufficient to maintain a field in an adjacent portion of said accumulation region and a surface of said substrate has a charge density sufficient to maintain an electric field in an adjacent portion of said accumulation region.
 17. The pixel cell of claim 16, wherein said sidewalls and said surface of said substrate each comprise a layer of high-k dielectric material.
 18. The pixel cell of claim 17, wherein said first conductivity type is p-type and said second conductivity type is n-type.
 19. The pixel cell of claim 18, wherein said charge density is negative charge density.
 20. The pixel cell of claim 18, wherein said layers of high-k dielectric material have an excess negative charge.
 21. The pixel cell of claim 20, wherein said high-k dielectric material is selected from the group consisting of aluminum oxide, aluminum nitride, and aluminum silicates.
 22. The pixel cell of claim 20, wherein said isolation trench is filled with a high-k dielectric material having an excess negative charge.
 23. The pixel cell of claim 17, wherein said sidewalls and said surface of said substrate further comprise a layer of dielectric material between said layer of high-k dielectric material and said substrate.
 24. The pixel cell of claim 23, wherein said dielectric material is silicon dioxide.
 25. The pixel cell of claim 17, wherein said first conductivity type is n-type and said second conductivity type is p-type.
 26. The pixel cell of claim 25, wherein said charge density is positive charge density.
 27. The pixel cell of claim 25, wherein said layers of high-k dielectric material have an excess positive charge.
 28. The pixel cell of claim 25, wherein said isolation trench is filled with a high-k dielectric material having an excess positive charge.
 29. The pixel cell of claim 16, further comprising a silicon dioxide layer in contact with said substrate.
 30. An imager device comprising: an image processor; and a pixel array for supplying signals to said image processor, at least one pixel of said array comprising: a substrate; a photodiode within said substrate; an isolation trench within said substrate; and a lining layer in said isolation trench, comprising a layer of high-k dielectric material; and a surface layer on a surface of said substrate located over said photodiode, comprising a layer of high-k dielectric material.
 31. The imager device of claim 30, further comprising a dielectric layer between said isolation trench and said lining layer.
 32. The imager device of claim 31, wherein said dielectric layer extends over said surface of said substrate, between said surface layer and said surface of said substrate.
 33. The imager device of claim 31, wherein said dielectric layer comprises silicon dioxide.
 34. The imager device of claim 30, wherein said lining layer has an excess charge sufficient to maintain a field in a first portion of an accumulation region of said photodiode.
 35. The imager device of claim 34, wherein said surface layer has an excess charge sufficient to maintain a field in a second portion of said accumulation region of said
 36. The imager device of claim 35, wherein said lining layer and said surface layer are high-k dielectric materials selected from a group consisting of aluminum oxide, aluminum nitride, and aluminum silicates.
 37. The imager device of claim 30, further comprising a filling layer located over said lining layer, filling said isolation trench.
 38. The imager device of claim 37, wherein said filling layer is selected from a group consisting of silicon dioxide, silicon nitride, oxide-nitride, nitride-oxide, oxide-nitride-oxide, and other insulating material.
 39. A pixel cell comprising: a photodiode in a substrate; an isolation trench in said substrate and having a bottom and sidewalls adjacent to said photodiode; a layer of silicon dioxide on said bottom and said sidewalls of said isolation trench; and a layer of aluminum oxide over said layer of silicon dioxide.
 40. The pixel cell of claim 39, further comprising a layer of silicon dioxide on a surface of said substrate over said photodiode.
 41. The pixel cell of claim 40, further comprising a layer of aluminum oxide over said layer of silicon dioxide on said substrate surface.
 42. The pixel cell of claim 39, wherein said isolation trench is filled with aluminum oxide.
 43. A method of forming a pixel cell comprising: forming an isolation trench in a substrate; forming at least a first high-k dielectric layer on a surface of said isolation trench; forming a buried photodiode in said substrate; and forming a second high-k dielectric layer on a surface of said substrate over said buried photodiode and said isolation trench.
 44. The method of claim 43, further comprising the step of forming a silicon dioxide layer over said surface of said isolation trench and said surface of said substrate before forming said first and second high-k dielectric layers.
 45. The method of claim 44, further comprising removing said silicon dioxide layer before forming said first and second high-k dielectric lining layers.
 46. The method of claim 43, further comprising the step of filling said isolation trench with a dielectric insulating material.
 47. The method of claim 43, wherein said first and second high-k dielectric layers are materials selected from the group consisting of aluminum oxide, aluminum nitride, and aluminum silicates.
 48. A method of forming a pixel cell comprising: forming an isolation trench in a substrate; forming a charge collection region in said substrate; forming a first accumulation region around said isolation trench, wherein said first accumulation region has an electric field near said isolation trench; and forming a second accumulation region between said charge collection region and a top surface of said substrate, wherein said second accumulation region has an electric field near said substrate surface.
 49. The method of claim 48, wherein the steps of forming said first and second accumulation regions include depositing a silicon oxide layer over sidewalls and a bottom of said isolation trench, and over said substrate surface.
 50. The method of claim 48, wherein the step of forming a first accumulation region includes depositing a first high-k dielectric material in said isolation trench.
 51. The method of claim 50, wherein the step of forming a second accumulation region includes depositing a second high-k dielectric material over said top surface of said substrate.
 52. The method of claim 51, wherein said first and second high-k dielectric materials are selected from the group consisting of aluminum oxide, aluminum nitride, and aluminum silicates.
 53. The method of claim 51, wherein said first and second accumulation regions are electron-rich accumulation regions.
 54. A method of forming a pixel cell comprising: forming a trench having a bottom and sidewalls in a substrate having a first conductivity type; forming a first high-k dielectric layer over said bottom and sidewalls of said trench; filling said trench with a layer of dielectric material; forming a charge-collection region having a second conductivity type in said substrate; forming an accumulation region having said first conductivity type over said charge-collection region and adjacent to said trench in said substrate; and forming a second high-k dielectric layer above said accumulation region over a top surface of said substrate.
 55. The method of claim 54, wherein said first conductivity type is p-type and said second conductivity type is n-type.
 56. The method of claim 55, wherein said first high-k dielectric layer is a material inducing hole-accumulation in said accumulation region adjacent to said trench.
 57. The method of claim 55, wherein said second high-k dielectric layer is a material inducing hole-accumulation in said accumulation region above said charge-collection region.
 58. The method of claim 55, wherein said first and second high-k dielectric layers are materials selected from the group consisting of aluminum oxide, aluminum nitride, and aluminum silicates.
 59. The method of claim 54, wherein said first conductivity type is n-type and said second conductivity type is p-type.
 60. The method of claim 54, further comprising the step of forming a silicon dioxide layer over said substrate after forming said trench and before forming said first and second high-k layers.
 61. The method of claim 60, further comprising the step of removing said silicon dioxide layer before forming said first and second high-k dielectric layers.
 62. The method of claim 54, further comprising forming a silicon dioxide layer between said first high-k dielectric layer and said bottom and said sidewalls of said trench.
 63. The method of claim 54, further comprising forming a silicon dioxide layer between said second high-k dielectric surface layer and said top surface of said substrate.
 64. A method of forming a pixel cell comprising: forming an isolation trench having a bottom and sidewalls in a p-type substrate; forming a layer of silicon dioxide on a bottom and sidewalls of said isolation trench; forming a layer of aluminum oxide on said bottom and said sidewalls of said isolation trench; forming a photodiode in said substrate adjacent to said isolation trench; forming a layer of silicon dioxide on a surface of said substrate over said photodiode and said isolation trench; and forming a layer of aluminum oxide over said substrate surface and said isolation trench.
 65. The method of claim 64, further comprising a step of filling said isolation trench with aluminum oxide before said step of forming a layer of silicon dioxide on a surface of said substrate over said photodiode and said isolation trench.
 66. The method of claim 64, further comprising steps of removing said silicon dioxide layers before said steps of forming a layer of aluminum oxide. 